產(chǎn)品信息 Product information

品牌

Brand

易來(lái)極

ELE KEY

材料類(lèi)型

Material Type

PP油性母粒

PP Oiliness Masterbatch

牌號(hào)

Geade

S0511

特性 Characteristic

·親油配方，提高油性顆粒物L(fēng)ipophilic formula to improve oily particles

·分散性能Excellent dispersion

·穩(wěn)定出絲Stable filament

·增大調(diào)機(jī)工藝參數(shù)窗口Increase the window of adjusting process parameters

外觀 Appearance

·圓柱狀 3.5-8mm    Cylindrical shape

顏色 Colour

·本白色            Natural

氣味 Smell

·接近無(wú)味          Almost tasteless

包裝Packing

·25KG/包           KG/ package

用途Applications

·熔噴無(wú)紡布        Melt Blown Monwoven

·與絕大多數(shù)的熔噴聚丙烯相熔性良好，直接添加，提高油性顆粒物過(guò)濾量，改善發(fā)硬變脆現(xiàn)象It has good fusibility with the majority of melt blown polypropylene and can be directly added to improve the filtration amount of oily particles and improve the hardening and embrittlement

通用性能 General Properties

序號(hào)

No.

性能

Properties

測(cè)試值

Value

單位

Unit

檢驗(yàn)方法

Method

測(cè)試條件

Test conditon

1

熔體流動(dòng)速率Melt Flow Index

200±100

g/10min

GB/T 3682

230℃，2.16kg

2

熔點(diǎn)Melting Point

160

℃

GB/T 19466

10℃/min

3

含水量Water content

< 0.03

%

GB/T 6283-2008

23℃  75%

4

密度density

0.90

g/cm3

GB/T 4472-2011

23℃  75%

5

建議添加量Recommended addition   10-20%

備注

Remarks

塑伯S0511油性顆粒物過(guò)濾量提升母粒是針對(duì)大部分客戶(hù)對(duì)于油性顆粒物過(guò)濾量要求（FFP2標(biāo)準(zhǔn)）推出的新產(chǎn)品。采用親油性的配方工藝，均勻分散于PP（聚丙烯）載體中，成絲后對(duì)油性顆粒物具有同性相吸效應(yīng)，對(duì)過(guò)濾量的提升與添加量成正比例（建議添加20%以下），隨著添加比例增加，熔體流動(dòng)性降低，故成型溫度應(yīng)同步提高。

SPP S0511 oil particle filter quantity promotion masterbatch is a new product launched for most customers' requirements for oil particle filter quantity (FFP2 standard).The formulation process with lipophilic property is adopted, which is evenly dispersed in PP (polypropylene) carrier. After being spun, it has the same phase absorption effect on oily particles. The increase of filtration amount is in positive proportion to the addition amount (it is suggested to add less than 20%). With the increase of the addition proportion, the melt fluidity decreases, so the molding temperature should be increased synchronously.